Symmetry

Stereogram of the magnetic point group: each operation applied to one direction. Filled = upper hemisphere, ring = lower; red operations include time reversal. Lines are mirrors; polygons are 2/3/4/6-fold axes; the centre ring is inversion.

Every structure in C 2 →

Atom sites · 47 sites · CSV

site	element	x	y	z	m_a	m_b	m_c	\|m\| (μ_B)
Ba1_1	Ba	0	0.9989	0.25
Ba1_2	Ba	0	0.0011	0.75
Ba1_3	Ba	0.1667	0.4989	0.25
Ba1_4	Ba	0.1667	0.5011	0.75
Ba2_1	Ba	0.0018	0.3333	0.0901
Ba2_2	Ba	0.9982	0.6667	0.9099
Ba2_3	Ba	0.1684	0.8333	0.0901
Ba2_4	Ba	0.1649	0.8333	0.4099
Ba2_5	Ba	0.1649	0.1667	0.9099
Ba2_6	Ba	0.1684	0.1667	0.5901
Mn1_1	Mn	0	0	0	4.08	0	0	4.08
Mn1_2	Mn	0.1667	0.5	0	−2.04	3.53	0	4.0771
Mn1_3	Mn	0.1667	0.5	0.5	2.04	−3.53	0	4.0771
Sb1_1	Sb	0.3307	0.3338	0.8474
Sb1_2	Sb	0.6693	0.6662	0.1526
Sb1_3	Sb	0.4974	0.8338	0.8474
Sb1_4	Sb	0.836	0.8338	0.6526
Sb1_5	Sb	0.836	0.1662	0.1526
Sb1_6	Sb	0.4974	0.1662	0.3474
O1_1	O	0	0.516	0.25
O1_2	O	0	0.484	0.75
O1_3	O	0.1667	0.016	0.25
O1_4	O	0.1667	0.984	0.75
O2_1	O	0.0932	0.2394	0.247
O2_2	O	0.9068	0.7606	0.753
O2_3	O	0.2599	0.7394	0.247
O2_4	O	0.0735	0.7394	0.253
O2_5	O	0.0735	0.2606	0.753
O2_6	O	0.2599	0.2606	0.747
O3_1	O	0.0031	0.8302	0.0862
O3_2	O	0.9969	0.1698	0.9138
O3_3	O	0.1697	0.3302	0.0862
O3_4	O	0.1636	0.3302	0.4138
O3_5	O	0.1636	0.6698	0.9138
O3_6	O	0.1697	0.6698	0.5862
O4_1	O	0.0895	0.0839	0.0801
O4_2	O	0.9105	0.9161	0.9199
O4_3	O	0.2561	0.5839	0.0801
O4_4	O	0.0772	0.5839	0.4199
O4_5	O	0.0772	0.4161	0.9199
O4_6	O	0.2561	0.4161	0.5801
O5_1	O	0.2514	0.0851	0.0909
O5_2	O	0.7486	0.9149	0.9091
O5_3	O	0.4181	0.5851	0.0909
O5_4	O	0.9152	0.5851	0.4091
O5_5	O	0.9152	0.4149	0.9091
O5_6	O	0.4181	0.4149	0.5909

Moment components are along the crystal axes a, b, c (μ_B), as magCIF writes them. Symmetry generates the rest of the cell from these sites.

Original file

sha256 of this copy: c0cdb33f514566752df8862b2819c45f9e6ade52fd4c065cd22a3593e47e159b
The mirror keeps the bytes Bilbao served, so the original should hash the same unless MAGNDATA has revised the entry since: shasum -a 256 1.0.46_Ba3MnSb2O9.mcif.

Magnetic group	C 2 BNS 5.13
Parent space group	C 2/c No. 15
Spins	coplanar · net moment 0 μ_B per cell
Propagation	[2/3 0 0] 1k
Cell	a 17.6526 · b 10.1863 · c 14.5522 Å · α 90° · β 90.43° · γ 90°
Transition	10 K (−263 °C)
Measured at	2.3 K
Magnetic ions	Mn
Largest moment component	4.08 μ_B
Method	NPD

Ba₃MnSb₂O₉

Symmetry

Source

Original file